S-Plastic Verton MV006BS is a compound based on Polypropylene (PP) containing Glass Fiber. Characteristics of this grade ar

Product Categories

Valox Plastic [1]
Ultem PEI Resin [197]
Cycoloy PC ABS [9]
Xenoy Resin [2]
Cycolac ABS [173]
Geloy Resin [110]
Colorcomp [20]
LNP Faradex [37]
S-Plastic Lubricomp [506]
LNP Stat Kon [308]
S-Plastic Thermocomp [705]
Plastic Resin Pellets Bulk [113]
Verton Plastic [106]

SAMTION INTERNATIONAL LIMITED

Contact Now

S-Plastic Verton MV006BS is a compound based on Polypropylene (PP) containing Glass Fiber. Characteristics of this grade ar

Name: SPlastic Verton MV006BS is a compound based on Polypropylene PP containing Glass Fiber Characteristics of this grade ar
Brand: S-Plastic Verton
Price: 1 USD

Cheap S-Plastic Verton MV006BS is a compound based on Polypropylene (PP) containing Glass Fiber. Characteristics of this grade ar for sale

Brand Name : S-Plastic Verton

Model Number : MV006BS

Certification : Datasheet，MSDS，ROHS，SGS，REACH，FDA，EU，UL，COC/COA ,please contact us

Place of Origin : ——

MOQ : 100KG

Price : *USD

Payment Terms : L/C, T/T, Western Union, MoneyGram

Supply Ability : To be negotiated

Delivery Time : To be negotiated

Packaging Details : 25KG/bag

Melt Volume Rate, MVR at 260°C/2.16 kg : ？？？

UL Recognized, 94HB Flame Class Rating (3) : ？？？

Contact Now

S-Plastics Verton MV006BS resin is a compound based on Polypropylene (PP) containing Glass Fiber. Characteristics of this grade are Heat

Property

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, yld, Type I, 5 mm/min	104	MPa	ASTM D 638
Tensile Stress, brk, Type I, 5 mm/min	104	MPa	ASTM D 638
Tensile Strain, yld, Type I, 5 mm/min	2.3	%	ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min	2.3	%	ASTM D 638
Tensile Modulus, 50 mm/min	6930	MPa	ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span	162	MPa	ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span	5840	MPa	ASTM D 790
Tensile Stress, yield, 5 mm/min	96	MPa	ISO 527
Tensile Stress, break, 5 mm/min	87	MPa	ISO 527
Tensile Strain, yield, 5 mm/min	2.2	%	ISO 527
Tensile Strain, break, 5 mm/min	2.2	%	ISO 527
Tensile Modulus, 1 mm/min	6330	MPa	ISO 527
Flexural Stress	145	MPa	ISO 178
Flexural Modulus, 2 mm/min	0	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	770	J/m	ASTM D 4812
Izod Impact, notched, 23°C	214	J/m	ASTM D 256
Multiaxial Impact	6	J	ISO 6603
Instrumented Impact Total Energy, 23°C	12	J	ASTM D 3763
Izod Impact, unnotched 80104 +23°C	53	kJ/m²	ISO 180/1U
Izod Impact, notched 80104 +23°C	20	kJ/m²	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	163	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	155	°C	ASTM D 648
CTE, -40°C to 40°C, flow	7.6E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	7.6E-05	1/°C	ASTM E 831
HDT/Bf, 0.45 MPa Flatw 80104 sp=64mm	162	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80104 sp=64mm	155	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Specific Gravity	1.09	-	ASTM D 792
Density	1.09	g/cm³	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.03	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)	0.3 - 0.6	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.5 - 0.8	%	ASTM D 955
Moisture Absorption (23°C / 50% RH)	0.02	%	ISO 62
Source GMD, last updated:2009/12/31

Processing

Parameter
Injection Molding	Value	Unit
Drying Temperature	80	°C
Drying Time	4	hrs
Melt Temperature	220 - 250	°C
Front - Zone 3 Temperature	250 - 260	°C
Middle - Zone 2 Temperature	245 - 255	°C
Rear - Zone 1 Temperature	230 - 245	°C
Mold Temperature	40 - 65	°C
Back Pressure	0.2 - 0.3	MPa
Screw Speed	30 - 60	rpm
Source GMD, last updated:2009/12/31

Other related products we recommend:

For more information please download the datasheet
	S-Plastics Verton MV006BS.pdf

Get The Latest Quotation

First-level distribution source in South China

Reduce procurement costs, improve supply stability,

Help you find the most suitable engineering plastic materials

Click to consult and get the latest quotation within 24 hours!

S-Plastic Verton MV006BS is a compound based on Polypropylene (PP) containing Glass Fiber. Characteristics of this grade ar